We supply a wide range of epoxies, silicones and polyurethanes for the manufacture of moulds for the ceramic and construction industries. Our polyurethanes are famous for its durability long functional life and shrinkage free properties.
| Product | Application | Mixing Ratio (weight) | Shore Hardness |
| Reckli Pur A55 Type K | pourable elastic two-component compound for making formliners, moulds and mould parts, block outs or recesses, nearly shrinkage-free curing, isometric reproduction od finest pattern details, long lasting functional life, universal type | 8:1 | A55 |
| Reckli Pur Compound 85 | two-component pourable resin for making high wear resistant moulds and moulds and mould parts in machinery, tool making, mould and model making, especially suitable for making blockouts or recesses in concrete industry | 3:1 | A85 |
| Reckli Epoxy OH | two componet surface-modified coating resin, thixotropic, for model and mould making, good resistance to plastic deformation, impact toughness and abrassion resistance, exact reproduction of mould pattern details, colour white | 7:1 |
| Plaster / Water Ratio (P/W) | 120% |
| Water / Plaster Ration (W/P) | 83% |
| Slump (Schmidt Ring) | 180-240mm |
| Initial Setting Time (Knife Set) | 10-14min. |
| Final Setting Time (Shore A) | 20-26min. |
| Granulometry: Over 150µm (dry screen) | ≤0.3% |
| Granulometry: Over 100µm (dry screen) | ≤0.5% |
| Absorption Capacity | ≥40% |
| Packing Size | 25 Kgs/Bag |
| Plaster / Water Ratio (P/W) | 135% |
| Water / Plaster Ration (W/P) | 74% |
| Slump (Schmidt Ring) | 170-220mm |
| Initial Setting Time (Knife Set) | 11-14min. |
| Final Setting Time (Shore A) | 17-25min. |
| Granulometry: Over 150µm (dry screen) | ≤0.2% |
| Expansion at 2 hours | ≤0.2% |
| Absorption Capacity | ≥35-45% |
| Packing Size | 25 Kgs/Bag |
| Plaster / Water Ratio (P/W) | 140% |
| Water / Plaster Ration (W/P) | 67% |
| Slump (Schmidt Ring) | 180-220mm |
| Initial Setting Time (Knife Set) | 10-14min. |
| Final Setting Time (Shore A) | 18-26min. |
| Granulometry: Over 150µm (dry screen) | ≤0.5% |
| Granulometry: Over 100µm (dry screen) | ≤0.8% |
| Bending Strength MOR | 60kg/cm2 |
| Packing Size | 25 Kgs/Bag |
| Plaster / Water Ratio (P/W) | 250% |
| Water / Plaster Ration (W/P) | 40% |
| Slump (Schmidt Ring) | 160-200mm |
| Initial Setting Time (Knife Set) | 7-12min. |
| Final Setting Time (Shore A) | 11-18min. |
| Granulometry: Over 150µm (dry screen) | ≤0.2% |
| Expansion at 2 hours | ≤0.2% |
| Bending Strength MOR | 80kg/cm2 |
| Packing Size | 25 Kgs/Bag |